Special High-Strength Geomembrane For Tailings Ponds And Landfills
Product Introduction
Smooth geomembrane is a kind of smooth surface geomembrane, which
is mainly made of high polymer materials such as high density
polyethylene (HDPE).
Product Properties
1. Excellent chemical corrosion resistance: can resist the erosion
of a variety of chemical substances, including acid, alkali, salt
and so on.
2. Large temperature range: can be used in a wide temperature
range, with good heat resistance and cold resistance.
3. Long service life: under proper use and maintenance conditions,
the service life of smooth geomembrane can be very long.
4. High tensile strength: with high tensile strength and
elongation, it can withstand certain water pressure and adapt to
foundation deformation.
5. Good impermeability: The use of plastic film impermeability,
effectively cut off the leakage channel, often used in waterproof
and impermeability projects.
Product Application
1. The impermeable layer of the landfill.
2. Waterproof layer of tailings storage yard.
3. Water conservancy projects in the channel seepage prevention,
dam seepage prevention.
4. Waterproofing measures in subway engineering.
5. Seepage prevention of artificial lakes, reservoirs and other
water bodies.
Product Specification
* Thickness(mm): 0.30mm~3.00mm
* Width:1m~9m
* Roll length: 30m~100m (customized request accept)
PS: Customized request accept for all above.
Geomembrane Series
Smooth HDPE Geomembrane For Landfill (GH-2S & GB/T 17643-2011)
| Specification | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | Remark |
| Item |
| Thickness (mm) | 0.75mm | 1.00mm | 1.25mm | 1.50mm | 2.00mm | 2.50mm | 3.00mm | |
| Density (g/c㎡,≥) | 0.939 | |
| Tensile Properties |
| Yield Strength (N/mm,LD/TD) | 11 | 15 | 18 | 22 | 29 | 37 | 44 | |
| Breaking Strength (N/mm,LD/TD) | 20 | 27 | 33 | 40 | 53 | 67 | 80 | |
| Yeild Elongation Rate (%) | 12 | |
| Breaking Elongation Rate (%) | 700 | |
| Rectangular Tear Strength (N) | 93 | 125 | 156 | 187 | 249 | 311 | 374 | |
| Puncture Strength (N) | 240 | 320 | 400 | 480 | 640 | 800 | 960 | |
Environmental Stress Crack Resistance (h)
(A single point of incision constant tensile method) | 300 | |
| Carbon Black |
| Carbon Black Content(Rang) (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Nine of 10 observation area should be grade 1 or grade 2, not more
than 1 of grade3 | |
| Oxidative Induction Time (OIT) |
| Standard OIT (min) | 100 | |
| High Pressure OIT (min) | 400 | |
| 85℃ Oven Ageing (Minimum Average) |
| 90 days after baking, the standard OIT retention(%) | 55 | |
| 90 days after baking, the hight pressure OIT retention(%) | 80 | |
| The Anti-UV Strength |
| Ultraviolet irradiation after 1600 hours, the standard OIT
retention(%) | 50 | |
| Ultraviolet irradiation after 1600 hours, the high pressure OIT
retention(%) | 50 | |
| -70℃ The Low Temperature Embrittlement Performance mpact | Pass | |
| Water Vapor Penetration Coefficient g.cm (cm2.s.Pa) | ≤1.0X10-13 | |
| Dimensional Stability | ±2 | |
Product Specification and Technical Index (GH-1 & GB/T 17643-2011)
Specification
Item | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | Remark |
| Thickness (mm) | 0.30 | 0.50 | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| Density (g/c㎡,≥) | 0.94 |
| Tensile Yield Strength (N/mm, ≥,LD/TD) | 4 | 7 | 10 | 13 | 16 | 20 | 26 | 33 | 40 | |
| Tensile Breaking Strength (N/mm, ≥,LD/TD) | 6 | 10 | 15 | 20 | 25 | 30 | 40 | 50 | 60 | |
| Yield Elongation Rate (%,≥,LD/TD) | - | - | - | 11 | |
| Breaking Elongation Rate (%,≥,LD/TD) | 600 | |
| Rectangular Tear Load (N,≥,LD/TD) | 34 | 56 | 84 | 115 | 140 | 170 | 225 | 280 | 340 | |
| Puncture Strength (N,≥) | 72 | 120 | 180 | 240 | 300 | 360 | 480 | 600 | 720 | |
| Carbon Black Content (%) | 2.0~3.0 | |
| Carbon Black Dispersion | Less than 1date of Grade 3 out of 10 data, grade 4,grade 5 is not
allowed | |